1600℃ Vacuum Furnace

---

1600℃ Carbide Cutting Tool Sintering Furnace

1. Features

Cemented carbide has a series of excellent properties such as high hardness, wear resistance, good strength and toughness, heat resistance and corrosion resistance, especially its high hardness and wear resistance. Change, still very high hardness at 1000 °C. The cutting speed of new cemented carbide tools is now hundreds of times that of carbon steel.

2. Types of Cemented Carbide

According to its application, cemented carbide can be basically divided into:

(1) Cemented carbide for cutting

(2) Cemented carbide mold

(3) Cemented carbide measuring tools

3. Wear-resistant Parts and Cemented Carbide for Mining and Petroleum Geology

Generally, wC-Co steels are mainly used for cutting tools for cast iron, non-ferrous metals and their alloys, metal drawing molds and medium-pressure molds, wear-resistant parts, measuring tools and mining and petroleum geological tools: WC-TIC-Co alloys are mainly used for Steel cutting,
WC-TIC-Tac (NbC)-Co alloys are mainly used for cutting difficult-to-machine materials.

4.Product Parameter

1400℃ Carbide Cutting Tool Sintering Furnace.

Models	Effective WorkingDimension (mm)	Max Temp.(℃)	UltimatePressure (Pa)	Pressure Rising Rate(Pa/h)	Temp.Uniformity (℃)	LoadingCapacity (kg)
RVS-226-H	200x200x600	1600/2200	6.7*10–3	0.67	±5	60
RVS-335-H	300x300x500	1600/2200	6.7*10–3	0.67	±5	100
RVS-446-H	400*400*600	1600/2200	6.7*10–3	0.67	±5	200
RVS-557–H	500*500*700	1600/2200	6.7*10–3	0.67	±5	300
RVS-669-H	600*600*900	1600/2200	6.7*10–3	0.67	±5	500
RVS-7710-H	700*700*1000	1600/2200	6.7*10–3	0.67	±5	700
RVS-8812-H	800*800*1200	1600/2200	6.7*10–3	0.67	±5	1000
RVS-9915-H	900*900*1500	1600/2200	6.7*10–3	0.67	±5	1200

1600℃  Vertical Vacuum Sintering Furnace

1. Model Specifications

There degumming – sintering – integration, pressure sintering furnace. Specifications are vertical, horizontal and other types.

2. Product Parameter

1600℃  Vertical Vacuum Sintering Furnace

Model	Effective Heating Zone (Φ*H)	Loading Capacity	MAX Temperature	Temperature Uniformity	Heating Power	Ultimate Vacuum	Pressure Rising Rate
RVS-V4030	Φ400*300mm	100Kg	1600℃	≤±5℃	40KW	6.67*10-3Pa	≤0.6Pa/h
RVS-V6045	Φ600*450mm	200Kg	1600℃	≤±5℃	80KW	6.67*10-3Pa	≤0.6Pa/h
RVS-V9065	Φ900*650mm	500Kg	1600℃	≤±5℃	120KW	6.67*10-3Pa	≤0.6Pa/h

1600℃ High Temperature Vacuum Sintering Furnace

1. Features

(1) The 1600℃ high-temperature vacuum sintering furnace can reduce some harmful components in the atmosphere, such as impurities in oxygen, water, nitrogen and other substances. For the pollution of some materials, it can avoid carburization, oxidation, decarburization, nitriding and reduction, etc. reaction.

(2) The high-temperature vacuum sintering furnace can allow the material to completely remove the particle oxide film before the liquid phase appears, thereby improving the wettability of the liquid phase and carbides, improving the structure of the alloy structure, and improving the performance of the alloy. .

(3) Because in a vacuum environment, the amount of gas in the pores of the compact will be reduced, so that the gas products will be more easily discharged from the pores or dissolved in the metal, so that the density of the material will be higher.

(4) The high-temperature vacuum sintering furnace can make the material wear resistance and strength higher, and can also reduce the production cost of the product, thereby saving budget.

Model	Temperature Uniformity Size(W*H*L)	Max. Temperature	Ultimate Pressure	Pressure Rising rate	Temperature Uniformity	Loading Capacity
RVS-335	300*300*500mm	1600℃	6.7*10-3Pa	0.67Pa/h	±5℃	75Kg
RVS-448	400*400*800mm	1600℃	6.7*10-3Pa	0.67Pa/h	±5℃	100Kg
RVS-559	500*500*900mm	1600℃	6.7*10-3Pa	0.67Pa/h	±5℃	150Kg
RVS-5511	500*500*1100mm	1600℃	6.7*10-3Pa	0.67Pa/h	±5℃	200Kg
RVS-669	600*600*900mm	1600℃	6.7*10-3Pa	0.67Pa/h	±5℃	200Kg
RVS-6611	600*600*1100mm	1600℃	6.7*10-3Pa	0.67Pa/h	±5℃	300Kg
RVS-6614	600*600*1400mm	1600℃	6.7*10-3Pa	0.67Pa/h	±5℃	500Kg
RVS-8812	800*800*1200mm	1600℃	6.7*10-3Pa	0.67Pa/h	±5℃	700Kg
RVS-8815	800*800*1500mm	1600℃	6.7*10-3Pa	0.67Pa/h	±5℃	1000Kg

1600℃ High Temperature Carbonization Furnace

1. Advantages

The high-temperature carbonization furnace adds a flue gas recovery device on the original basis to achieve dust-free carbonization process. The recovered flue gas is purified
After discharge, it can be ignited like liquefied gas, and can be used twice. This kind of carbonization equipment consumes less electricity in the production process.
The charcoal furnace in the charcoal machine adopts high-tech purification technology and uses high-temperature resistant heavy metal steel. The advantage of charcoal stove is sturdiness
Durable, no deformation, no oxidation, excellent heat preservation effect and performance, easy operation and reliable.

2. Product Parameter

1600℃ High Temperature Carbonization Furnace

Model	Loading space size	Designtempreture	Rated temperature	Heating voltage	power	Ultimate vacuum	Temperature uniformity	Loading weight
	mm	℃	℃	V	KW	Pa	℃	KG
IVG-150C	800X800X1200	1650	1600	50	150	20	±10	800
IVG-210C	1000X1000X1500	1650	1600	50	210	20	±10	1500
IVG-300C	1300X1300X2000	1650	1600	50	300	20	±15	3000
IVG-550C	1500X1500X3000	1650	1600	50	550	20	±15	5000
IVG-1200C	2500X2500X4000	1650	1600	50	1200	20	±15	10000
IVG-1500C	2500X2500X5000	1650	1600	50	1500	20	±15	15000

1600℃ Carbon Felt Insulation Blanket Carbonization Furnace

1. 1600℃ Carbon felt insulation blanket carbonization furnace introduction

Mainly used in carbon/carbon composites, hard insulation blankets, curing blankets, carbon fiber insulation materials, graphite products and other medium and low temperature carbonization process, but also for other materials carbonization.

2. Product Parameter

Model	Loading space size	Design  tempreture	Rated temperature	Heating voltage	power	Ultimate vacuum	Temperature uniformity	Loading weight
	mm	℃	℃	V	KW	Pa	℃	KG
IVG-150CI	□800X800X1200	1650	1600	50	150	20	±10	800
IVG-210CI	□1000X1000X1500	1650	1600	50	210	20	±10	1500
IVG-300CI	□1300X1300X2000	1650	1600	50	300	20	±15	3000
IVG-550CI	□1500X1500X3000	1650	1600	50	550	20	±15	5000
IVG-1200CI	□2500X2500X4000	1650	1600	50	1200	20	±15	10000
IVG-1500CI	□2500X2500X5000	1650	1600	50	1500	20	±15	15000

Shanghai Geheng Vacuum Technology Co., Ltd. is a vacuum heat treatment furnace manufacturer with many years of experience in design, manufacturing and production. Mainly produce vacuum heat treatment furnace, vacuum sintering furnace, vacuum brazing furnace, New Energy And Environmental Protection Equipment and other vacuum equipments.Provide customized services, equipment work area can be based on customer output.